Nippon Yakin Kogyo Co., Ltd
Nippon Yakin Kogyo NASH880 Heat Resistant Alloys
Manufacturer: Nippon Yakin Kogyo Co., Ltd
Model : NASH880
NASH880
Heat Resistant Stainless Steel
NASH880 is an austenitic stainless steel developed by Nippon Yakin. It is suitable for use in high-grade sheathed heater tubes and provides excellent corrosion resistance in wet environments such as hot water supply devices. Nippon Yakin supplies NASH880 in sheet and strip forms.
| Chemical Composition | 25Ni-28.5Cr-1.2Mo-0.3Al-0.3Ti | |
|
Product Shape |
 Coil |
|
| Weldability | NASH880 welded tube has good formability. There is no crack on the bead after several forming tests. | |
| Blackening Property | Emissivity of NASH880 after blackening heat treatment is the same level as alloy 800 (Low C%). | |
| Heat Treatment | Heat treatment of NASH880 can be performed in the same manner as with other austenitic stainless steels. The heat treatment temperature range is as follows: | |
| – Solution treatment: 1000–1100°C; water cooling. | ||
| Applications | Sheathed heater, Furnace parts. | |
SheetSteel Grade/Standard
| Nippon Yakin Grade | JIS | ASTM | EN |
|---|---|---|---|
| NASH880 | — | — | — |
Chemical Composition
| C | Si | Mn | P | S | Ni | Cr | Mo | Cu | Al | Ti | Co | N | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Specification (NASH880) | ≤0.030 | 0.30–0.50 | 0.35–0.65 | ≤0.025 | ≤0.015 | 24.50–27.00 | 22.80–23.90 | 1.15–1.35 | ≤0.25 | 0.20–0.40 | 0.25–0.45 | 0.05–1.00 | ≤0.02 |
Physical Properties
| Density [g/cm³] | 7.92 |
|---|---|
| Specific heat [J/kg•K] | 462 |
| Electrical resistivity [μΩ•cm] | 92.5 |
| Thermal conductivity [W/m•K] | 12.3 |
| Average coefficient of thermal expansion [10⁻⁶/°C] | 25–200°C 15.6 |
| 25–400°C 16.4 | |
| 25–600°C 17.2 | |
| 25–800°C 18.0 | |
| Young’s modulus [MPa] | 19.4 × 10⁴ |
| Magnetism [μ] | None |
| Melting range [°C] | 1380–1407 |
Mechanical Properties
Mechanical Properties at Room Temperature
| 0.2% proof stress [MPa] | Tensile strength [MPa] | Elongation [%] | |
|---|---|---|---|
| Specification (NASH880) | ≥205 | ≥520 | ≥30 |
| Example Cold-rolled sheet 0.5 mm |
280 | 587 | 42 |
High Temperature Strength
Corrosion Resistance
1. Crevice Corrosion Resistance
Test condition:
- ① Multicreviece test piece
- ② Test temperature: 80°C
- ③ Test time: 24 hr
| NaCl | 5% | 10% |
|---|---|---|
| alloy825 | ○ | ○ |
| NASH880 | × | × |
| alloy 800 (Low C%) | × | × |
2. Stress Corrosion Cracking Resistance
Test condition:
- ① U-bend test piece
- ② Liquid solution: 10% NaCl
- ③ Test time: 74 hr
| Temperature | 180°C | 200°C | 220°C |
|---|---|---|---|
| alloy825 | ○ | ○ | ○ |
| NASH880 | × | × | × |
| alloy 800 (Low C%) | − | − | − |
Weldability
NASH880 welded tube has good formability.
There is no crack on the bead after several forming tests.
 |
 |
 |
|
Flaring test |
Flattening test |
180° Bending test (R=14mm) |
Formability of NASH880 welded tubes (8mmφ × 0.5mm)
Blackening Property
Emissivity of NASH880 after blackening heat treatment is the same level as alloy 800 (Low C%).
 |
 |
Heat Treatment
Heat treatment of NASH880 can be performed in the same manner as with other austenitic stainless steels. The heat treatment temperature range which is normally used is as follows:
- Solution treatment: 1,000-1,100°C; water cooling.
Applications
- Sheathed heater
- Furnace parts.
Related Products
-
Nippon Yakin Kogyo NAS825 Corrosion Resistant Alloys
-
Nippon Yakin Kogyo NAS601 Heat Resistant Alloys
-
Nippon Yakin Kogyo NASH38X Heat Resistant Alloys
-
Nippon Yakin Kogyo NAS630 High Strength Stainless Steels
-
Nippon Yakin Kogyo NAS329J3L Corrosion Resistant Alloys
-
Nippon Yakin Kogyo NAS354N Corrosion Resistant Alloys
REQUEST QUOTATION
PAYMENT
LINK