Nippon Yakin Kogyo Co., Ltd
Nippon Yakin Kogyo NASH330 Heat Resistant Alloys
Manufacturer: Nippon Yakin Kogyo Co., Ltd
Model : NASH330
NASH330 (UNS N08330)
Heat-Resistant Nickel Alloy
NASH330 is a heat-resistant nickel alloy with excellent high-temperature strength, corrosion resistance, and metallurgical stability. In particular, it provides superior resistance to carburization and nitridation. Because it has a fully austenitic microstructure, it displays good workability. Nippon Yakin supplies NASH330 in plate, sheet, and strip forms.
| Chemical Composition | 33Ni-18Cr-1.2Si | ||
| Product shape |  Coil |  Sheet |  Plate |
| Workability | The hot workability and cold workability of NAS-H330 are similar to those of conventional austenitic stainless steels. For hot working, a starting temperature of 1230°C and finishing temperature of 850°C are suitable. Cold workability is similar to that of conventional austenitic stainless steels. Work hardening tends to be slightly lower. Bending, drawing, and similar working are possible. | ||
| Weldability | NAS-H330 can be welded by TIG, MIG, and shield metal arc welding in the same manner as with conventional standard austenitic stainless steels. Manufacturers frequently use AWS ERNiCr-3 welding electrodes. | ||
| Heat Treatment | Heat treatment of NAS-H330 is similar to that of conventional austenitic stainless steels. The typical heat treatment is as follows: Solution heat treatment: 1040-1120°C.The solution heat treatment process performs carbide dissolution and strain removal. | ||
| Pickling | Pickling is performed with a nitric hydrofluoric acid solution or aqua regia solution (nitric hydrofluoric acid solution) in the same manner as with standard austenitic stainless steels. | ||
| Features | NAS-H330 is used mainly in high temperature carburizing or nitriding atmospheres. It is most suitable for application in the 815-1150°C temperature range. | ||
Steel Grade/Standard
| Nippon Yakin Grade | JIS | ASTM B536 |
|---|---|---|
| NASH330 | — | UNS N08330 |
Chemical Composition
| C | Si | Mn | P | S | Ni | Cr | Cu | Pb | Sn | Fe | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Specification (UNS N08330) | ≤0.08 | 0.75-1.50 | ≤2.00 | ≤0.03 | ≤0.03 | 34.0-37.0 | 17.0-20.0 | ≤1.00 | ≤0.005 | ≤0.025 | Bal. |
Physical Properties
| Density [g/cm³] | 7.98 |
| Specific heat [J/kg•K] | 480 |
| Electrical resistivity [μΩ•cm] | 100 |
| Thermal conductivity [W/m•K] | 11.9 |
| Average coefficient of thermal expansion [10⁻⁶/°C] | 25–200°C 15.3 |
| 25–400°C 16.0 | |
| 25–600°C 16.5 | |
| 25–800°C 17.1 | |
| Young’s modulus [MPa] | 19.6 × 10⁴ |
| Magnetism [μ] | None |
| Melting range [°C] | 1340–1395 |
Mechanical Properties
Mechanical Properties at Room Temperature
| 0.2% proof stress [MPa] | Tensile strength [MPa] | Elongation [%] | Hardness [HRBW] | |
|---|---|---|---|---|
| Specification ASTM B536 (UNS N08330) | ≥207 | ≥483 | ≥30 | — |
| Examples Hot-rolled plate (9.5mm) | 253 | 549 | 46 | 78 |
| Examples Cold-rolled sheet (3mm) | 269 | 545 | 45 | 76 |
Microstructure
| Specification ASTM B536 (UNS N08330) | Heat treatment |
|---|---|
| — | ≥1040°C |
Typical microstructure of NASH330
Grain Size Number = 5
Work Hardening Property
High Temperature Strength
Allowable Stress
Workability
The hot workability and cold workability of NASH330 are similar to those of conventional austenitic stainless steels. For hot working, a starting temperature of 1230°C and finishing temperature of 980°C are suitable. Cold workability is similar to that of conventional austenitic stainless steels. Work hardening tends to be slightly lower. Bending, drawing, and similar working are possible.
Weldability
You can weld NASH330 using TIG, MIG, and shielded metal arc welding, just as you do with conventional standard austenitic stainless steels. Manufacturers frequently use AWS ERNiCr-3 welding electrodes.
Heat Treatment
Heat treatment of NASH330 is similar to that of conventional austenitic stainless steels. The typical heat treatment is as follows:
Solution heat treatment: 1040–1120°C
Carbide dissolution and strain removal are performed in the above solution heat treatment.
Pickling
Pickling is performed with a nitric-hydrofluoric acid solution or aqua regia solution (nitric-hydrochloric acid solution) in the same manner as with standard austenitic stainless steels.
Features
NASH330 is used mainly in high-temperature carburizing or nitriding atmospheres. It is most suitable for application in the 815–1150°C temperature range.
Applications
Furnace parts, Heat treatment fixtures, Carbonization furnace components.
Related Products
-
Nippon Yakin Kogyo NAS254N Corrosion Resistant Alloys
-
Nippon Yakin Kogyo NASNM15M Non-Magnetic Alloys
-
Nippon Yakin Kogyo NASH840 Heat Resistant Alloys
-
Nippon Yakin Kogyo NAS255NM Corrosion Resistant Alloys
-
Nippon Yakin Kogyo NASH880 Heat Resistant Alloys
-
Nippon Yakin Kogyo NAS800H, NAS800T Heat Resistant Alloys