Japan, Nitta
Nitta Polysprint™ Belt
Product Made in Japan
Manufacturer: Nitta
Model: Polysprint™ Belt
No adhesives necessary – allowing for simple and fast installatiPolysprint™ Belton.
Features
Produced using a wide variety of material combinations such as thermoplastic polyurethane, nitrile rubber and elastic fabrics and featuring varied surface constructions from smooth to structured.
Easy and fast finger jointing system without using any glue, this range provides excellent dimension stability and is highly suitable for small pulley diameters. Our PolySprint™ belts are suitable for high speed and use the unique Nitta NBR rubber with fine textured surfaces.
Applications
Our PolySprint™ range of belts is ideal for feeding, folding and packaging and are installed in printing (web) folders, print finishing applications, packaging machines, live roller and textile applications.
Construction Example
Product List – Elastic Type
BELT TYPE | TOP SURFACE |
BOTTOM SURFACE |
SURFACE MATERIAL |
MAIN APPLICATIONS | THICKNESS [MM] |
SPECIFIC TENSION [N/MM WIDTH] | MINIMUM PULLEY DIAMETER [MM] |
---|---|---|---|---|---|---|---|
TA09 | TPU/TPU | Mail sorter, bank note insertion conveyor | 0.9 | 0.4 (at 5 % elongation) |
20 | ||
TA12 | TPU/TPU | Mail sorter, packaging | 1.2 | 0.2 (at 2 % elongation) |
25 | ||
TA-S6 | TPU/TPU | Mail sorter | 0.9 | 0.6 (at 5 % elongation) |
25 | ||
NTA | Knit/TPU | Mail sorter, packaging | 1.0 | 0.5 (at 5 % elongation) |
25 | ||
TC | TPU/TPU | Mail sorter | 1.4 | 0.3 (at 2 % elongation) |
40 | ||
HTA09 | Hard TPU/TPU | Mail sorter, bookbinding | 0.9 | 0.5 (at 5 % elongation) |
25 | ||
STC-10 | Knit/TPU | Stacker | 1.35 | 0.5 (at 5 % elongation) |
25 | ||
GTD | NBR/TPU | Postal, Paper | 1.45 | 1.1 (at 5% elongation) |
25 | ||
SNTC-RB22A | Soft TPU (Longitudal Groove)/Knit | Inclined, Declined Conveyor | 2.25 | 0.3 (at 2% elongation) |
25 | ||
SNTC-TW18A | Soft TPU (Mini Rough Top)/Knit | Inclined, Declined Transport | 1.8 | 0.3 (at 2% elongation) |
20 |
TPU: Thermoplastic Urethane
* 2 Actual color may slightly differ from the image you see.
Product List – Polyester Fabric Type
BELT TYPE | TOP SURFACE |
BOTTOM SURFACE |
SURFACE MATERIAL |
MAIN APPLICATIONS | THICKNESS [MM] |
SPECIFIC TENSION [N/MM WIDTH] | MINIMUM PULLEY DIAMETER [MM] |
---|---|---|---|---|---|---|---|
DB-4E14 | TPU/TPU | Mail sorter | 1.4 | 4 (at 1 % elongation) |
25 | ||
FZ-5E12 | Coated NBR/NBR | Printing/bookbinding | 1.25 | 5 (at 1 % elongation) |
35 | ||
LA-4E14 | NBR/NBR | Printing/bookbinding/roller conveyor | 1.4 | 4 (at 1 % elongation) |
20 | ||
NB-2E10 | TPU/Knit | Sheeter | 1.0 | 2 (at 1 % elongation) |
15 | ||
RT-22E70-2 | NBR/Fabric | Conveying corrugated board, Flexo folder gluer | 7.0 | 10 (at 0.5 % elongation) |
100 | ||
TFL-15E20 | NBR/NBR | Roller conveyor, Textile | 2.0 | 15.0 (at 1% elongation) |
25 | ||
TFL-15E25 | NBR/NBR | Textile | 2.5 | 15.0 (at 1% elongation) |
30 | ||
TFL-22E26-2 | NBR/NBR | Ring Spinning, OE, TFO | 2.6 | 22.0 (at 1% elongation) |
50 | ||
TFL-22E26C-2 | NBR/NBR | Covering machine | 2.6 | 22.0 (at 1% elongation) |
50 | ||
TLA-30E30-2 | NBR/NBR | DTY | 3.0 | 30.0 (at 1% elongation) |
70 | ||
TTF-4E10 | Fabric/Fabric | Bookbinding | 1.0 | 4 (at 1 % elongation) |
15 | ||
TTP-8E18N | Fabric/Fabric | Printing & Book Binding | 1.8 | 8.0 (at 1% elongation) |
40 | ||
TTZ-4E10LF | Fabric/NBR coated fabric | Printing & Book Binding | 1.0 | 4.0 (at 1% elongation) |
30 | ||
XH-8E30 | NBR/NBR | Folder Gluer; Paper Manufacturing | 3.0 | 8.0 (at 1% elongation) |
40 | ||
XH-8E40 | NBR/NBR | Folder Gluer; Paper Manufacturing | 4.0 | 8.0 (at 1% elongation) |
50 | ||
XH-8E55 | NBR/NBR | Folder Gluer; Paper Manufacturing | 5.5 | 8.0 (at 1% elongation) |
80 | ||
XHTG-15E34 | NBR/Fabric | Cardboard Conveyor; Table Supported Conveyor | 3.4 | 7.0 (at 0.5% elongation) |
50 |
The tension after 200 hours of running (23 °C , 50 %RH).
* Actual color may slightly differ from the image you see.
* Types other than above are also available.
* Technical data is not stated.
* The specification is subject to change for improvement without notice.
* Should you require any further information, please contact us.