Chemical, Isolite Insulating, Japan
Isolite Insulating LBK Insulating Firebrick
Manufacturer: Isolite Insulating
LBK Insulating Firebrick
Features
Hot Surface and Back-up lining insulation
LBK Series are the world’s highest level of super lightweight Insulating Firebrick. LBK Series are using for Hot Surface and Back-up lining insulation, and it has a characteristic of light weight, low thermal conductivity, low heat storage, small reheat shrinkage, high thermal stability and suitable for superior resistance to reductive atmosphere.
Typical Applications
Hot face expose and back-up lining of Annealing Furnace, Carburizing Furnace, Galvanizing Furnace, Carbon Baking Furnace, Heat treatment Furnace, Hot Stove, Clacking Furnace, Reformer, Incinerator.
Quality
| LBK-20 | LBK-23 | LBK-26 | ||
| Specification | Reheat Shrinkage Not More Than 0.5% when tested at （℃） | 1200 | 1300 | 1400 |
| Cold Crushing Strength [MPa] JIS R 2615 | 0.59≦ | 0.78≦ | 0.98≦ | |
| Modules of Rupture [MPa] JIS R 2619 | 0.49≦ | 0.69≦ | 0.78≦ | |
| Thermal Conductivity at 350℃±10℃[W/m・K] JIS R 2616 | 0.17≧ | 0.19≧ | 0.24≧ | |
| Chemical Composition Fe₂O₃ (%) | 1.5≧ | 1.5≧ | 1.0≧ | |
| Test Result | Bulk Density (g/cm3) | 0.48 | 0.52 | 0.59 |
| Cold Crushing Strength [MPa]JIS R 2615 | 1.4 | 2.0 | 2.9 | |
| Modules of Rupture [MPa] JIS R 2619 | 1.0 | 1.2 | 1.4 | |
| Thermal Conductivity at 350℃±10℃[W/m・K] JIS R 2616 | 0.16 | 0.17 | 0.23 | |
| Rehear Shrinkage (%) at ( )℃X8hr JIS R 2613:1985 | 0.03（1200） | 0.19（1300） | 0.14（1400） | |
| Chemical Composition (%) Al₂O₃ | 41 | 41 | 57 | |
| JIS R 2216 SiO₂ | 51 | 51 | 39 | |
| Fe₂O₃ | 1.3 | 1.3 | 0.8 |
| LBK-28 | LBK-30 | LBK-3000 | ||
| Specification | Reheat Shrinkage Not More Than 0.5% when tested at （℃） | 1500 | 1550 | 1600 |
| Cold Crushing Strength [MPa] JIS R 2615 | 2.0≦ | 3.0≦ | 3.0≦ | |
| Modules of Rupture [MPa] JIS R 2619 | 1.0≦ | 1.5≦ | 1.3≦ | |
| Thermal Conductivity at 350℃±10℃[W/m・K] JIS R 2616 | 0.27≧ | 0.30≧ | 0.37≧ | |
| Chemical Composition F₂O₃ (%) | 1.0≧ | 1.0≧ | 1.0≧ | |
| Test Result | Bulk Density (g/cm3) | 0.70 | 0.75 | 0.8 |
| Cold Crushing Strength [MPa] JIS R 2615 | 4.0 | 5.0 | 6.4 | |
| Modules of Rupture [MPa] JIS R 2619 | 1.7 | 1.9 | 1.8 | |
| Thermal Conductivity at 350℃±10℃[W/m・K] JIS R 2616 | 0.25 | 0.28 | 0.34 | |
| Rehear Shrinkage (%) at ( )℃X8hr JIS R 2613:1985 | 0.10（1500） | 0.33（1550） | 0.26（1600） | |
| Chemical Composition (%) Al₂O₃ | 72 | 69 | 71 | |
| JIS R 2216 SiO₂ | 26 | 30 | 28 | |
| Fe₂O₃ | 0.6 | 0.4 | 0.4 |
Related Products
-
Seiwa E10MP145 Electromagnetic Wave Control Sheet EMC Products
-
Super Tool PJTC3065B-65165B/3065C-65165C Jig Plate (Cross T-Slot Type) (16 / 18)
-
Yamamoto Easy 450B Poweful Handle Cylinder Gun
-
Nippon Chemical Screw PTFE/W(d-D-t) PTFE/Washer
-
Matsuo Valve JIS F7358 Lift Check Globe Valve
-
Ross Asia Directional control valve [SV27 series] Safety cat. 2 PL c, 2/2-way valve, external monitoring